Microsilex

February 12th, 2008

InfoNOW!

Have someone from GCC
contact you with more information Click Here

Company: GCC

Microsilex is a product based on natural silica with pozzolanic properties which can improve performance and durability concrete and mortar manufactured with Portland Cement.

Color:

Microsilex is light brown in color and adding this product does not affect the final concrete color. Besides, it is compatible when adding iron oxide based pigments for concretes with integrated color.

Uses and applications:

Microsilex must be used as an additive in proportion with the cement weight in concrete or mortar mixes. It may be used as an additive for cement or as a cement substitute. In concrete mixes it can be used in constructions such as: pavement, ducts, bridges, residual water tanks, etc.

Advantages:

When used in concrete mixes, Microsilex increases the resistance in the later stages (from 28 days on). It improves shapeability, reduces permeability, increases sulphate resistance, helps to control the alkali-aggregate reaction and increases concrete abrasion resistance.

Physical and chemical characteristics:

Chemical properties	ASTM C-618	Microsilex
SiO ₂ + Al2O ₃ + Fe ₂O ₃ (%)	70.0 minimum	91.30
SO ₂ (%)	4.0 maximum	0.14
Humidity (%)	3.0 maximum	1.25
Loss due to ignition (%)	10.0 maximum	0.38
Alkalis such as (%)	1.5 maximum	0.05

Physical properties	ASTM	Microsilex
Fineness when sifted through a No 325 (45 um) mesh pass. %	ASTM C-430 76.0 minimum	96.0
Resistance to sulphates up to 180 days (%)	ASTM C-1012 0.05 maximum	0.03
Alkali-silica reaction up to 180 days (%)	ASTM C-227 0.05 maximum	0.02
Density gr/cm ³	ASTM C-188 Does not apply	2.3
Amount of water required (control %)	ASTM C-311 115 maximum	106
Pozzolanic activity index up to 7 days (control %)	ASTM C-311 75 minimum	105
Pozzolanic activity index up to 28 days (control %)	ASTM C-311 75 minimum	122
Expansion in mortar up to 14 days (%)	ASTM C-1260 0.1 maximum	0.06